çukura yerleştirme

listen to the pronunciation of çukura yerleştirme
التركية - الإنجليزية
{i} pitting
The formation of pits on a surface because of corrosion
(Mühendislik) Pitting or pitting corrosion, is a form of extremely localized corrosion that leads to the creation of small holes in the metal
The appearance of small depressions or cavities produced during solidification or corrosion
the formation of small pits in a surface as a consequence of corrosion
A condition on bits that is caused by the presence of foreign material such as rock cutting or the use of rock drill oil with a high sulphur content
A form of wear characterized by the presence of surface cavities, the formation of which is attributed to processes such as fatigue, local adhesion, cavitation or corrosion
Gal-vanic attack under moist and acidic conditions between molecular structures of differing alloy content
A form of extremely localized attack characterized by holes in the metal Pitting is one of the most destructive and insidious forms of corrosion Depending on the environment and the material, a pit may take months, or even years, to become visible
present participle of pit
A small depression in the surface of the decoration, perhaps caused by tiny bubbles in the glaze, or if a sharp rough spot is present, perhaps caused by spalling fire brick
The presence of pin holes or small craters in the solder joint caused by oxidation, plating material or other foreign incompatible matter Such joints are generally also dull in finish
(Inter-Crystalline Corrosion) -- Galvanic attack under moist and acidic conditions between molecular structures of differing alloy content
Corrosion type, for which the electrolytic metal removal extends only on small surface areas and results in the formation of local cavities (crater-shaped, pinhole-type) Because the amount of the produced corrosion products is only small, pitting is mostly recognized only when leakages occur
Highly localised corrosion in which penetration into the metal occurs, with consequent danger of perforation [back] [top]
Forming small sharp cavities in a metal surface by nonuniform electro-deposition or by corrosion
Damage to a metal surface that takes the form of one or a series of small craters or pits in the surface This is a type of failure often seen in worn-out bearing cones
Forming small sharp cavities in a metal surface by non-uniform electrode position or by corrosion
Localised surface defects on metals, in the form of small depressions, or "pits"
çukura yerleştirmek
pit
çukura yerleştirme